Ultrasonic Inspection of Pipeline Circumferential Butt welds

18 Aug 2024 Download PDF

What are Pipeline Circumferential

Pipelines are an integral part of all industry processes in all sectors worldwide. Transporting liquids, gases, and solids through above ground, buried and subsea pipes, the condition of the pipework is essential to the safety and continued operation of the processes they are a part of.

A pipelines main vulnerability is located at the welded joints connecting sections of the line. The welding process introduces heat affected zones that lead to structural changes in the metal that weaken the part in the weld area, the fatigue resistance, is lowered and the overall strength and toughness can be affected.

Additional failure mechanisms can be introduced during service, these can include;

• Temperature fluctuations
• External corrosion from the environment or water held in lagging
• Internal flow erosion
• High pressure cycling
• System vibration
• Mechanical damage

Methods of mitigating these issues are available but the weld should always be considered a point of weakness and be regularly inspected to monitor its condition.

          Figure 1 – Pipeline welding and on site image of pipework

Inspection Methods

 

Multiple inspection methods exist to assess pipeline welds, these include surface methods such as Visual, Magnetic Particle, Dye Penetrant and Eddy Current inspection, these only inform the inspector on the condition of the surface and slight subsurface of the weld. Full volumetric inspection requires Ultrasonic methods (UT) or Radiography (RAD).

UT has many advantages over RAD, the main ones being.

• UT produces no radiation hazard and can be carried out alongside other personnel; this is a safer process than radiography and means the site does not need to be cleared of workers for the inspection to take place.

UT is sensitive to small defects, cracking defects and planar lack of fusion defects making it a great application for thinner pipework but is also applicable for thicker materials.

 

Figure 2 – Ultrasonic inspection of Butt welds on pipe sections

Inspection Challenges of Circumferential Butt Welds

 

The most common circumferential weld geometry is pipe to pipe, both sides are the same material and same thickness, but this is not always the case, a pipe section can be welded to fittings such as bends, reducers, tees, and flanges which can be different thicknesses, made of cast materials and have attachments restricting access for inspection. All of these are points to consider when choosing the correct ultrasonic method for the inspection.

 

Figure 3 – Examples of Butt weld configurations that can be encountered

Types of Ultrasonic Inspection

Conventional Ultrasonic Inspection (UT)

UT utilizes single or dual crystal transducers in single beam configurations to interrogate a weld. Transducers are set to produce specific known angles in the material (usually 0°, 45°, 60° and 70°, but other angles can be used) manual ‘scanning’ or movement of the transducer on the surface ensures coverage of the weld, return signals are interpreted by the inspector to detect and size defects.

See our application note for more information

 

 

 

Figure 4 – Example of how conventional UT interacts and displays a defect

Phased Array (PA)

A PA inspection is carried out using a transducer containing multiple individual elements in an array. These elements are pulsed individually or in groups to create a beam that can be directed and focused depending on the requirements of the inspection. PA inspection can inspect full weld volumes in a single sweep or interrogate specific areas of a weld and produces a recorded data file with views that can be manipulated to aid interpretation.

See our application note for more information

 

Figure 5 – Examples of how a PA S-Scan interacts with defects

 

Full Matrix Capture / Total Focusing Method (FMC/TFM)

FMC is a form of data capture utilizing PA transducers, individual elements are pulsed, and A-Scan data is recorded by each of the remaining elements, this process is repeated for each element in turn creating a large set of data. TFM is a method of processing and displaying an FMC data set, an area of interest is chosen as a resolution set. FMC takes each pixel in this area and averages the total number of A-Scans for this pixel, creating a new A-Scan. As this is the average of 100s or 1000s of A-Scans, it reduces noise and is focused on this pixel. Repeating this for each pixel creates a view where the scan is focused at every pixel in the area.

See our application note for more information

Figure 6 – example of defect detection display of PA (Left) and TFM (Right)

Time of Flight Diffraction (TOFD)

TOFD utilizes two transducers set apart and facing each other in a ‘pitch-catch’ formation. One transducer sends a pulse into the material and the other transducer receives. Instead of using reflections from defects and displaying results as depth of reflection or beam path, TOFD detects ‘tip diffraction signals’ which are much weaker and displays results in time of flight. This gives a technique that has a high accuracy to defect depth and through wall height and is often used in the calculations for fracture mechanics.

See our application note for more information

Figure 7 – ToFD scan showing defect signals

 

CTA: For further information or support, please contact the Sonatest Applications Team: applications@sonatest.com